Resin flooring system Resucoat™ Profile S

Epoxy flooring coating system suitable for:

  • Food processing and beverage areas.
  • Chemical plant rooms.
  • Engineering workshops.
  • Automotive and aviation areas.
  • Factory units.
  • Warehouses.
  • Suitable for all demarcation and walkways.


A high build epoxy resin system with a light non-slip texture achieved by adding an aggregate to the mix which stays suspended whilst the product is installed for a consistent finish. Applied by roller and paint brush, the system is low odour and provides a textured gloss coloured finish at approximately 500 micrometres thickness, which is suitable for all areas of industry where a hard-wearing non-slip and chemically resistant floor coating is required.

Features and benefits:

  • High build finish.
  • Non-slip performance.
  • Solvent-free.
  • Hygienic and easily cleaned.
  • Good colour stability.
  • Excellent slip resistance with the inclusion of selected aggregates.
  • High gloss finish.
  • Available in a wide range of colours.

General information


High gloss


12 Standard colours plus Ral's available

Consult manufacturer for options


High build finish, non-slip performance, solvent-free, hygienic and easily cleaned, good colour stability, excellent slip resistance with the inclusion of selected aggregates.


Epoxy resin


System thickness: 0.5 mm

Uniclass 2015

Ss_30_42_54_75 Resin flooring systemsPrimary


M12/10 Resin flooring

M12/110 Resin flooring

Specification data - Resin flooring systems Enhanced data




Moisture content to BS 8204


Substrates must be clean, sound, dry and free of surface laitance with a minimum strength of 25 N/mm². Mechanically prepare substrate to provide a surface texture that will function as a key for the resin. Remove all dust and debris. Repair significant mechanical damage, pitting and cracks


Resuseal WB Clear (optional)

Resin flooring

Resucoat HB

Base coat

Resucoat HB with aggregate mix

Top coat

System thickness

0.5 mm

Reaction to fire (to EN 13501-1)

Bfl - s1

Curing time

12–16 hours

(at 20ºC) Light traffic

48–72 hours

(at 20ºC) Designed traffic

≤7 days

(at 20ºC) Full cure traffic

Abrasion resistance

134.7 mg loss/ 1000 cycles

to ASTM D4060-14


9.6 MPa

to BS EN ISO 604


7.5 MPa

to BS EN ISO 527-2

Flexural strength

3.2 N/mm²

to BS EN 13892-8

Bond strength

>3 N/mm²

to BS EN 13892 (substrate failure)

Temperature resistance

Tolerant of temperatures up to 45°C

Chemical resistance


UV stabilization


Slip resistance


to BS 7976-2

Environmental information

Country of material origin

United Kingdom

Similar products from Sherwin-Williams