Resin Flooring System Acrydur™ RA

Name: Resin Flooring System Acrydur™ RA
Brand: Sherwin-Williams
SKU: tKFeWujzCGJZR72p1EzrtE

Verified by manufacturer 25 days ago

Sherwin-Williams

Methyl methacrylate (MMA) car park ramp floor system.

Jump to:

+44 (0)1204 521771 Website

Application

For use in:

Car park ramps.
Baggage handling area ramps.
External vehicle ramps.
Heavy duty plant and traffic areas.

Description

Acrydur Topfloor RA is a 6 mm thick, fast curing MMA resin flooring system for car park ramps and similar heavy duty vehicle applications. The finish features a scratch coat and base coat with quartz aggregate scatter and a coloured topcoat to create a tough finish suitable for cars and other vehicles.

Acrydur Topfloor RA creates traction and reduces skidding and noise from traffic movement.

Features and benefits:

Coloured finish.
High chemical resistance.
Reduced tyre squeal and noise.
Good slip and skid resistance.
Hard-wearing.
Non-dusting.
Curing time of 1–2 hours (light traffic); 3–4 hours (designed traffic).
UV stable.
FerFa class 5–6.

General information

Color	Grey Blue Beige Yellow Red Green Show more
Finish	Textured
Material	Methyl methacrylate Resin Quartz Aggregate
Shape	Formless
Length	Bespoke
Width	Bespoke
Height	6 mm

Uniclass	Ss_30_42_54_75 Resin flooring systemsPrimary
CAWS	M12/110 Resin flooring M12/10 Resin flooring

Specification data - Resin flooring systems

Substrate	-
Testing	Moisture content to BS 8204.
Preparation	Preparation of existing substrates. Guidance for specification option: Substrates must be clean, sound, dry and free of surface laitance with a minimum strength of 25 N/mm². Mechanically prepare substrate to provide a surface texture that will function as a key for the resin. Remove all dust and debris. Repair significant mechanical damage, pitting and cracks.
Primer	Acrydur PR01. Acrydur PR02.
Resin flooring	Quartz aggregate scatter.
Surface treatment	Acrydur TC04 Colour.

Basecoat	Acrydur ME04 slurry. Guidance for specification option: Using 0.2–0.3 mm silica sand. Manufacturer guidance And scratchcoat.
Joints	Not required. Epo-Flex™ VJ. Guidance for specification option: The spacing and type of joints should be determined prior to the resin floor system being installed. Mix Epo-Flex VJ Part A (base) with Epo-Flex VJ Part B (hardener). These units are in pre-weighed containers. Mix using a low speed mixer and paddle (300–400 rpm) for 2–3 minutes, until a uniform mixed product is obtained. Apply the Epo-Flex VJ immediately to the prepared and cut joints with a knife to a consistent smooth finish.
System thickness	6 mm.
CompressiveStrength	To DIN 1164, 25 N/mm².
TensileStrength	To DIN 1164, 15 N/mm².
Bond strength	>1.5 Mpa.
Water permeability	Impermeable.
Slip resistance	To BS 7976-2:2002 + A1:2013, >36 wet/ dry.
Application temperature	5–30ºC.