NBS Source
I'm a manufacturer

Resin Flooring System FasTop® Multi DP

Verified by manufacturer 6 months ago

Sherwin-Williams

Hygienic Polyurethane cement floor screed with aggregate for added slip resistance

Jump to:
+44 (0)1204 521771 Website

Application

For use in:

  • Food manufacture and processing.
  • Brewing and beverage processing.
  • Pharmaceutical manufacturing.
  • Heavy duty plant and traffic areas.
  • Dairies.
  • Commercial kitchens.
  • Abattoirs and meat processing.
  • Areas requiring high slip resistance.
  • Chillers

Description

FasTop Multi DP is a heavy-duty polyurethane cement screed designed to create uniform slip-resistant finishes whilst providing thermal shock resistance for a variety of industrial environments.


FasTop Multi DP is laid between 5-9 mm and then broadcast with quartz, granite or carborundum aggregate to give a heavy non-slip finish designed to provide low slip potential in areas that are wet and/ or exposed to greases and oils. The system is overcoated with FasTop Multi T150 to seal the aggregate in and provide a hard wearing and long-lasting surface. The system is designed to work with the current modular FasTop resins and hardeners.


Features and benefits:

  • High or very high slip resistance.
  • High chemical resistance.
  • Resistant to hot water up to 90 degrees centigrade at 5mm thickness
  • Resistant to freezing temperatures
  • Hard-wearing.
  • Matt finish.
  • 22.1 kg pack size.
  • 36 month shelf life.
  • CE approved.
  • FerFa class: 7.
  • Light traffic after 12-18 hours
  • Full curing time of five to seven days (at 20°C).
  •  Campden BRI approved as non-taint.
  • HACCP certified.

General information

Color

Black

Blue

Grey

Green

Red

Show more

Finish

Matt

Material

Polyurethane

Resin

Quartz

Granite

Carborundum

Show more

Shape

Formless

Length

Bespoke

Width

Bespoke

Height

-

Manufacturer guidance

5–7 mm.

Warranty description

Other

Uniclass

Ss_30_42_54_75 Resin flooring systemsPrimary

CAWS

M12/110 Resin flooring

M12/10 Resin flooring

Specification data - Resin flooring systems

Substrate

-

Preparation

Preparation of new substrates.

Guidance for specification option:

New concrete must be clean, sound, dry, fully cured and surface laitance removed by vacuum enclosed shot blasting or mechanical grinding, a minimum strength of 25 N/mm² is required.

Preparation of existing substrates.

Guidance for specification option:

Existing concrete floors:

Remove all dirt, oil, grease, old paint or any other surface contaminants by vacuum enclosed shot blasting, scarifying or mechanical grinding. Fats, oils or greases must be removed by mechanical means and detergent washing and making sure all residue of detergent is washed and removed by rinsing with clean water. Local repairs should be carried out using FasTop Multi BU.


Existing floors (previously coated):

All previous coatings and loose floor paints must be removed by mechanical preparation as described in the above section and primed as specified. If the old resin flooring cannot be removed then please consult with our technical team for advice on intercoat adhesion and suitability, as it may not be compatible with the existing floor coating.

Levelling screed

FasTop Multi DP.

Primer

FasTop Multi Primer.

Resin flooring

Quartz aggregate.

Carborundum aggregate.

Granite aggregate.

Overcoating

FasTop Multi T150.

Shore Hardness - D

To BS ISO 7619-1:2010, 80.

Abrasion resistance

BS EN 13892-4:2002, AR 4.

CompressiveStrength

To BS EN 604:2003, 34.6 MPa.

TensileStrength

BS EN 13892-2:2002, 2.4 N/mm².

Flexural strength

To BS EN 6319-7:1985, 5.8 N/mm².

Bond strength

To BS EN 13813, B 3.0.

Impact resistance

BS EN ISO 6272-1:2011, >4.

Temperature resistance

Up to 90°C at 5 mm.

Application temperature

5–20°C.

Reaction to fire

To BS EN 13501-1:2018, Bfl–s1.

System thickness

5–7 mm.

Slip resistance

To BS 7976-2:2002+A1:2013, <36 (low slip potential in dry/ wet conditions).

Coverage

22.1 kg will cover 2.20 m²/L at 5 mm.
22.1 kg will cover 1.83 m²/L at 6 mm.

VOC content

9 g/L.

Density

2 g/cm³ (mixed).