Resin Flooring System Acrydur™ TD

Verified by manufacturer 6 months ago

Sherwin-Williams

Methyl methacrylate (MMA) top deck car park floor system.

Jump to:
+44 (0)1204 521771 Website

Application

For use in:


  • Top deck car parks.
  • Baggage handling areas with vehicles.
  • External vehicle areas and walkways.
  • Heavy duty plant and traffic areas.

Description

Acrydur Topfloor TD is a 6 mm thick, fast curing MMA resin flooring system for top deck car parks and similar heavy duty vehicle applications. The finish typically features a flexible membrane with crack bridging properties, and a base coat with a quartz aggregate scatter and a coloured topcoat to create a tough finish suitable for cars and other vehicles. 


Acrydur Topfloor TD reduces noise from traffic movement and delivers a coloured finish for new projects or refurbishments.


Features and benefits:


  • Flexible crack bridging system for dynamic movement suitability.
  • Coloured finish.
  • High chemical resistance.
  • Reduced tyre squeal and noise.
  • Good slip and skid resistance.
  • Hard-wearing.
  • Non-dusting.
  • UV stable.
  • FerFa class 5–6.
  • Cure time of 1–2 hours (light traffic); 3–4 hours (designed traffic).

General information

Color

Finish

Textured

Material

Methyl methacrylate

Resin

Quartz

Aggregate

Shape

Formless

Length

Bespoke

Width

Bespoke

Height

6 mm

Uniclass

Ss_30_42_54_75 Resin flooring systemsPrimary

CAWS

M12/110 Resin flooring

M12/10 Resin flooring

Specification data - Resin flooring systems

Substrate

-

Testing

Moisture content to BS 8204.

Preparation

Preparation of existing substrates.

Guidance for specification option:

Substrates must be clean, sound, dry and free of surface laitance with a minimum strength of 25 N/mm². Mechanically prepare substrate to provide a surface texture that will function as a key for the resin. Remove all dust and debris. Repair significant mechanical damage, pitting and cracks.

Primer

Acrydur PR01.

Acrydur PR02.

Guidance for specification option:

With optional broadcast of 0.4–0.8 mm silica sand at 300 gr/m².

Resin flooring

Silica quartz scatter.

Surface treatment

Acrydur TC04.

Acrydur TC05 colour.

Basecoat

Acrydur ME04 slurry.

Guidance for specification option:

Using 0.2–0.3 mm silica sand.

Joints

Not required.

Epo-Flex™ VJ.

Guidance for specification option:

The spacing and type of joints should be determined prior to the resin floor system being installed.


  • Mix Epo-Flex VJ Part A (base) with Epo-Flex VJ Part B (hardener). These units are in pre-weighed containers.
  • Mix using a low speed mixer and paddle (300–400 rpm) for 2–3 minutes, until a uniform mixed product is obtained.
  • Apply the Epo-Flex VJ immediately to the prepared and cut joints with a knife to a consistent smooth finish.


Membrane

Acrydur ME01.

Guidance for specification option:

With crack bridging fabric if required.

CompressiveStrength

To DIN 1164, 25 N/mm².

TensileStrength

To DIN 1164, 15 N/mm².

Bond strength

>1.5 MPa.

Water permeability

Impermeable.

Slip resistance

To BS 7976-2:2002 + A1:2013, >36 wet/ dry.

Application temperature

5–30ºC.

System thickness

6 mm.