Arbomeric MP10
Verified by manufacturer 2 months ago
A one part, low modulus, modified polymer sealant for lightweight cladding, blockwork and brickwork.
Application
Suitable for use in perimeter sealing in curtain walling and polyester powder coated frames, structural joints in brickwork and blockwork, and joints in lightweight cladding.
Description
A one part, low modulus, modified polymer sealant which cures, on exposure to moisture vapour, to form an elastic rubber.
Features and benefits:
- Not recommended for floor joints.
- Very good UV resistance.
- Anticipated service life in excess of 20 years.
General information
Color | Black Grey White Other |
Material | Polymer Rubber |
Shape | Formless |
Uniclass | |
CAWS | H11/775 Bonding sealants for structural sealant/ bonded glazing |
Product range |
Specification data - Construction joint sealants
Standard | To BS EN ISO 11600. |
Material | One part modified polymer. |
Class | F-20LM. |
Colour | Black.Buff.Grey.Limestone.Portland.White. |
Accessories | None. Arbo Primer 2650. Arbo Cleaner No. 16. Guidance for specification option: Alcohol Based. Arbo Cleaner No.17. Guidance for specification option: Xylene based, not suitable for use with plastics or delicate finishes. |
Application temperature | +5 to +35ºC. |
Service temperature | -40 to +90ºC. |
Working time | Skin time at 20º C and 65% relative humidity: 30 minutes. |
Hardness (shore A) | 30. |
Cure time | 1-2 mm per 24 hours at 20ºC and 65% relative humidity. |
UV resistance | Very good. |
Anticipated service life | 20 years+. |
Chemical resistance | Resistant to most dilute acids and alkalis. Guidance for specification option: Organic solvents may cause the sealant to swell and lose adhesion. |
Compression strength | Butt joints (movement in tension and compression): 70%. Guidance for specification option: Must not exceed ± 33% in any one direction. |
ShearStrength | Lap joints (movement in shear): 125% Guidance for specification option: Must not exceed ± 66% in any one direction. |
Modulus at 100% elongation | 0.29 N/mm². |
Elongation at break | 550%. |
TensileStrength | 0.45 N/mm². |
Joint width | 6 mm (minimum single application); 25 mm (maximum single application); 35 mm (maximum multiple applications). Guidance for specification option: Joint depth:
Manufacturer guidanceWidth: depth ratio (within above minimum/ maximum restrictions):
|