To Specify a full Intumescent Fire Protection Coating System C1-C4 (Primer + Intumescent + Topcoat) click on the link below and add to your Chorus Specification:

Intumescent Fire Protection Coating Systems (C1–C4) - C1–C4 Corrosivity & Fire Protection | Hempel A/S | NBS Source (thenbs.com)

To Specify a full Anti-Corrosion System C1-C5 (No Intumescent Fire Protection) (Primer + Topcoat) click on the link below and add to your Chorus Specification :

Anti-Corrosion Protective Coating System (C1–C5) - For Corrosive Environments | Hempel A/S | NBS Source (thenbs.com)

For further advice on Specifications please contact Ian Morton at iam@hempel.com

Hempathane HS 55610

A two-component glossy acrylic polyurethane topcoat, cured with aliphatic isocyanate, with good gloss and colour retention.

Features and benefits:

Contains zinc phosphate.
May be specified as a one-coat "Direct To Metal" system in environments classified as C2 and C3.
Maximum, dry exposure only: 120°C/248°F.
Approved as a low flame spread material when used as part of a predefined paint system.
Compatible with Hempel Intumescent coatings.
For severely corrosive atmospheric environment.
High volume solids.
The minimum temperature for curing is -10°C [14°F].

Product compatibility:

Previous coat: According to Hempel’s Specification. Recommended products are: Hempaprime Multi 500 45950/3, Hempadur Quattro series, Hempadur Avantguard series.
Subsequent coat: None.

Application method:

Airless spray, brush or roller.

Drying times: Determined for dry film thickness 80 µm [3.1 mils] at standard conditions. Indicative values at 20ºC; Touch dry: 90 minutes, Hard dry: Five hours.

For more details on the product please refer to Product Datasheet in the Associated Content.

EPD - Hempathane HS 55610