Sikadur 32 - Structural Two-part Bonding Agent
Verified by manufacturer 1 year ago
Moisture tolerant, structural, two-part bonding agent, based on a combination of epoxy resins and special fillers. For bonding, fixing and anchoring with sustainable benefits.
Application
For use as a structural bonding agent and adhesive for:
- Concrete elements (including bonding fresh to hardened concrete)
- Hard natural stone
- Ceramics, fibre-cement
- Mortar, bricks, masonry
- Steel, iron, aluminium
- Wood
- Polyester/ fibreglass and epoxy resin materials
- Glass
Description
Moisture tolerant, structural, two-part bonding agent, based on a combination of epoxy resins and special fillers.
For bonding, fixing and anchoring with sustainable benefits.
Features and benefits:
- Designed for use at temperatures between +10°C and +30°C.
- Easy to mix and apply.
- Suitable for dry and damp concrete surfaces.
- Very good adhesion to most construction materials.
- High bond strength.
- Hardens without shrinkage.
- Different coloured components (for mixing control).
- No primer needed.
- High initial and ultimate mechanical strength.
- Impermeable to liquids and water vapour.
- Good chemical resistance.
General information
Color | Grey Guidance for specification option: When mixed. White base with black hardener. |
Uniclass | |
CAWS | Z22/310 Joints E40/530 Sealant Z22/310 Joints Z20/390 Adhesives Z20/390 Adhesives generally E40/530 Sealant |
Specification data - Epoxy resin-based bonding compounds
Carrier | Manufacturer's standard. |
Total VOCs (maximum) | Manufacturer's standard. |
Form | Two-component. |
Fire resistance | Reaction to fire, to EN 13501-1: Class C-s1,d0/ class Bfl-s1. |
Type | Sikadur®-32 Normal. Sikadur®-32+. |
Density | 1.5 kg/L (±0.1). Guidance for specification option: Mixed resin at 23°C. |
Compressive strength (mean value) | To EN 12190, 61 N/mm². Guidance for specification option: Consult manufacturer's literature for details based on curing time and temperature. |
Modulus of elasticity | To ASTM D695: ~3300 N/mm² (14 days at +23 °C); to EN 13412: ~5000 N/mm². |
Flexural strength | Manufacturer's standard. Guidance for specification option: Consult manufacturer's literature for details based on curing time and temperature. |
Modulus of elasticity | To ASTM D695: ~3300 N/mm² (14 days at +23 °C); to EN 13412: ~5000 N/mm². |
Elongation at break | To EN ISO 527-2: 1.4% (±0.1; 14 days at +23 °C). |