Very easy to apply, single component, fast curing, highly elastic, UV-resistant waterproofing with very good adhesion to numerous substrates.
For waterproofing concrete slabs, flat roofs, terraces or balconies, wet and damp rooms and similar applications. It has excellent adhesion to most substrates (including masonry, concrete, screed, Polyvinyl chloride (PVC), fibre-reinforced plastic (FRP), plastics, metal, and bitumen) and high elasticity.
A single component, liquid applied, elastic, crack bridging waterproofing material based on MS Polymer technology. It is characterized by excellent adhesion to a wide variety of building materials and can be applied on dry or slightly moist substrates. It is liquid applied and therefore seamless, which greatly eases application to complicated architectural details. Due to its UV stability, it is suitable for internal and external use. It is quickly resistant to rain.
The fast curing coating is solvent free and does not contain isocyanates. It is highly flexible, resistant to occasional foot traffic, aging, hydrolysis, UV-rays, salts and frost. CE marked to BS EN 1504-2.
When applying over concrete, the substrate must first be primed with Köster Construction Resin or Köster LF-BM, which is then broadcast with kiln-dried silica sand to increase adhesion.
Warranty description | Ten year |
Uniclass | |
CAWS | J30/110 Cold-applied tanking |
Application thickness | 1.5–2 mm. |
Consumption (per layer applied) | 1.5–2.5 kg/m². |
TensileStrength | 1.3 N/mm². Guidance for specification option: At 23°C. |
Elasticity | 500%. |
Overcoating | 24 H. Guidance for specification option: Overcoating time. |
Cure time | 24–48 H. Guidance for specification option: Full cure time at 23°C. |
Density | 1.5 g/cm³. |
Application temperature | 5–35°C. |
Service temperature | -25 to +80°C. |
Third-party certification | CE marked to BS EN 1504-2. |
Contains Red List materials | No |
Recyclability | No |
Recycled contentAs defined in clause 7.8 of BS EN ISO 14021 | 0 % |