Elladur™ Deco Flake Screed is a multi-component polyaspartic/ polyurea fast cure floor system which utilizes coloured flakes applied to 10 mm epoxy screed to provide a very heavy duty decorative flooring finish. Elladur™ Deco Flake Screed is approved as IMO high performance flooring.

System includes:

  • Substrate.
  • Primer: Resuprime MVT.
  • Base coat: Resuscreed 55.
  • Intermediate coat: Elladur SF.
  • Broadcoat: Coloured flakes.
  • Grout coat: Elladur SF Clear (optional second coat).
  • Seal coat: Resupen WB Matt Clear.

Features and benefits:

  • Produces decorative and functional surface.
  • Fast curing even at low temperatures.
  • Ultraviolet (UV) stable.
  • Solvent-free.
  • Very low odour.
  • Tough but flexible.
  • Can be applied onto a wide range of substrates.

Applications:

  • Where a heavy duty, high build UV stable system is required.
  • Areas where fast turnaround but high performance finishes are required for commercial, light industrial and transport areas.
  • Decorative floor areas.
  • Domestic areas.
  • Retail spaces.

General information
Specification data
Product Reference

Elladur™ Deco Flake Screed

Colour

Clear

Standard product features

Technical characteristics:

  • System thickness: 11 mm.
  • Hardness after 24 hours, Shore D to BS ISO 7619-1: 83.
  • Abrasion resistance to BS EN 13892-5: AR 1.
  • Tensile strength to BS EN ISO 527-2: 12.2 N/mm².
  • Bond strength to EN 13892-8: >3 N/mm² (substrate failure).
  • Temperature resistance: Up to 70⁰C at 3 mm.
  • Reaction to fire to BS EN 13501-1: Bfl – s1.
  • Chemical resistance: Good.
  • Ultraviolet (UV) stable: Yes.
  • FerFa class: Class 6.
  • Volatile organic content (VOC): Varies depending on product, 12–84 g/L.
  • Coverage per unit: Varies depending on product, up to 50 m².
  • Cure rate: Depends on traffic conditions and temperature: 8 hours to 8 days.
  • Application temperature: 10–25°C and an equilibrium relative humidity (ERH) <90%.