The screed is suitable for floors in homes, offices, public buildings and places exposed to similar loads. It may be applied as a levelling screed directly onto a load bearing floor, unbonded on a separating barrier, or as a floating floor and is particularly suited in conjunction with underfloor heating or cavity floors. Can be covered with a floor finish such as tiles, linoleum, parquet, cork or carpet. If a cement based adhesive or smoothing compound is required the surface of the screed must first be sealed, using an appropriate acrylic primer/ sealer.

Description

Südanit 300 Anhydrite Screed is a pumpable, high quality screed material based on calcium sulfate. It is designed for application at thicknesses of between 20 and 90 mm.

Benefits:

  • Pumpable, high flowability.
  • Early trafficking.
  • Very low shrinkage.
  • Reduced drying times.
  • CE marked.
  • Anhydrite binder complies with EN 13454-1:2004.

Applications:

The screed is suitable for floors in homes, offices, public buildings and places exposed to similar loads. It may be applied as a levelling screed directly onto a load bearing floor, unbonded on a separating barrier, or as a floating floor and is particularly suited in conjunction with underfloor heating or cavity floors. Can be covered with a floor finish such as tiles, linoleum, parquet, cork or carpet. If a cement based adhesive or smoothing compound is required the surface of the screed must first be sealed, using an appropriate acrylic primer/ sealer.

General information
Specification data - Ready-mixed trowelled calcium sulfate screeds
Product Reference

CASEA Südanit 300 Calcium Sulfate Floor Screed

Standard product features

Technical characteristics:

  • Maximum thickness: 90 mm.
  • Minimum thickness: Bonded, 20 mm. Unbonded, 30 mm. Domestic, 35 mm. Commercial, 40 mm. Over underfloor heating pipes: 25 mm (BS 8204-7).
  • Use: Internal.
  • Compressive strength (28 days): > 25 N/mm².
  • Flexural strength (28 days): > 5 N/mm².
  • Tensile adhesion: > 1.5 N/mm².
  • Shrinkage (28 days): < 0.1%.
  • Hardening time (before foot traffic): 8–12 hours.
  • Recommend water content: 14–16%.
  • Reaction to fire: A1 non-combustible.
  • Thermal conductivity: 1.6 W/mK.
  • Flow rate: 220 – 260 mm.
  • Calcium sulfate content: ≥ 85%.
  • Shrinkage: ≤ 0.2 mm/m.