I'm a manufacturer

Application

Suitable for use on glass balustrades.

Description

Arbokol 682 Pouring Grade is a two-part epoxy polysulphide sealant, which when the components are mixed together, cures to form an extremely tough sealant with a small degree of movement accommodation.


Features and benefits:

  • Has a self-levelling formulation for quick and ease of use.
  • The product has good adhesion to glass, concrete, stone, metals and many other common building substrates.
  • It can also be transferred to cartridges or a bulk loading gun before being applied.
  • Very good UV resistance.
  • Expected service life of 20 years.

General information

Color

Grey

Material

Polysulphide

Shape

Formless

Uniclass

Pr_30_31_76_63 Polysulfide glazing compounds and sealantsPrimary

CAWS

E40/530 Sealant

L30/50 Purpose-made balustrades

L30/510 Wood balustrades

L30/515 Wood balustrades

L30/55 Proprietary balustrades

L30/550 Purpose-made balustrades

L30/560 Proprietary balustrades

Product range

Polysulphide Sealants
Sealants and Facades

Specification data - Polysulfide glazing compounds and sealants

Standard

To BS 6180.

Sealant type

Two part.

Colour

Grey.

Accessories

None.

Arbo Cleaner No. 17 (Xylene based).

Guidance for specification option:

Not suitable for use with plastics or delicate finishes.

Arbo Cleaner No. 16 (Alcohol based).

Application temperature

+5 to +40ºC.

Service temperature

-15 to +70ºC.

Working time

Work life (typical at 20ºC): 1.5–2 hours.

Hardness (shore A)

95.

Guidance for specification option:

Cured at +20ºC.

Shore Hardness - D

50.

Guidance for specification option:

Cured at +20ºC.

Curing time

Cure rate at +20ºC/ 65% RH: 7 days.

Guidance for specification option:

At lower temperatures cure rate will be slowed down.

Chemical resistance

Resistant to most dilute acids and alkalis, petrol, diesel, jet fuel, vegetable oils and many common solvents.

UV resistance

Very good.

ExpectedServiceLife

20 years.

Compression strength

Butt joints: 5% movement accommodation.

Guidance for specification option:

Movement in tension and compression.

Breaking load

Force at break (7 days cure, tests on a 12 x 12 x 50 mm joint): 2500 N.