Sikaflex®-113 Rapid Cure - Construction adhesive

Verified by manufacturer 1 year ago

Sika Limited

Fast curing construction adhesive.

Jump to:
+44 (0)1707 394444 Website

Application

For internal and external use. An adhesive to bond most construction components and materials such as:

  • Concrete.
  • Masonry.
  • Most stones.
  • Ceramic.
  • Wood.
  • Metals.
  • Glass.

Description

A one-part, fast curing adhesive with very high initial grab which bonds most common construction substrates.


Features and benefits:

  • Fast curing.
  • Early handling after 20 minutes.
  • Compatible with with EPS/ XPS.
  • Adhesive-sealant with CE marking.
  • Very low emissions.


Approvals/ standards:

  • CE Marking and Declaration of Performance to EN 15651-1 - Sealants for non-structural use in joints in buildings - Facade elements: Class F EXT-INT 12,5P.


Environmental information:

  • Conformity with LEED v4 EQc 2: Low-Emitting Materials.
  • VOC emission classification GEV-EMICODE EC 1PLUS.
  • VOC emission classification of building materials RTS M1.
  • Class A+ according to French Regulation on VOC emissions.

General information

Color

White

Black

Material

Silane

Polymer

Shape

Formless

Uniclass

Pr_30_31_76_16 Construction joint sealantsPrimary

CAWS

H51/610 Sealant joints

E40/530 Sealant

F30/610 Movement joints with sealant

H13/750 Structural sealant joints

H13/740 Sealant joints

F30/76 Movement joints with sealant

M40/75 Sealant movement joints

H51/610 Sealant joints

H40/785 Sealant jointing

H42/661 Sealant joints

E40/530 Sealant

H42/661 Sealant joints

Specification data - Construction joint sealants

Standard

To EN 15651-1.

Material

Single-part polymer.

Class

F-12.5P.

Colour

White.

Black.

Fire performance

-

Reaction to fire

Class E.

Base

Silane terminated polymer.

Manufacturer guidance

Chemical base.

Density

To ISO 1183-1, ~1.50 kg/l.

Shore A hardness

To ISO 868, ~55.

Guidance for specification option:

After 28 days.

TensileStrength

To ISO 37, ~2.5 N/mm².

Elongation at break

To ISO 37, ~350%.

ShearStrength

To ISO 17178, ~0.9 MPa (1 hour); ~1.9 MPa (24 hours); ~2.4 MPa (7 days).

Guidance for specification option:

At 23°C/ 50 % r.h, 0.1 mm thickness.

Manufacturer guidance

Lap shear strength.

Tear resistance

To ISO 34, ~6.0 N/mm.

Service temperature

−40 to +60°C.

SAG

To ISO 7390, ~1 mm.

Guidance for specification option:

20 mm profile, 23°C.

Manufacturer guidance

Sag flow.

Ambient temperature

5–35°C.

Guidance for specification option:

Minimum–maximum.

Substrate

5–35°C.

Guidance for specification option:

Minimum–maximum, 3°C above dew point temperature.

Manufacturer guidance

Substrate temperature.

Curing time

~4 mm/ 24 h.

Guidance for specification option:

  • 23°C/ 50% r.h.
  • Skin time (CQP 019-1): ~12 min, 23°C/ 50% r.h.

Manufacturer guidance

CQP 049-2.

Similar products from Sika Limited

Everbuild Tecnic® Hybriflex 40  - Hybrid based adhesive

Everbuild Tecnic® Hybriflex 40  - Hybrid based adhesive

Everbuild Tecnic® Hybriflex 55 - Building and construction adhesive

Everbuild Tecnic® Hybriflex 55 - Building and construction adhesive

Sikaflex®-112 Crystal Clear - Adhesive and sealant

Sikaflex®-112 Crystal Clear - Adhesive and sealant

Sikaflex®-118 Extreme Grab - Construction adhesive

Sikaflex®-118 Extreme Grab - Construction adhesive

Sikaflex®-508

Sikaflex®-508