Application

For the protection of concrete floors and decks subject to trafficking in the most demanding internal and external environments.

Description

Two component epoxy and cementitious modified polymer coating for the protection of concrete floors in demanding environmental conditions. It incorporates advanced cement chemistry, metakaolin, fibre, epoxy and styrene acrylic copolymer technology to provide multi-functional protection. When mixed, it exhibits a high degree of flow to enable ease of application by pouring or pumping techniques to give a smooth surface finish. It hydrates rapidly to form a dense, hard wearing, durable coating, which exhibits both polymeric and resinous properties, giving low permeability to water and providing very high chemical and abrasion resistance to ensure long term performance.

Features/ Benefits:

  • Excellent abrasion and impact resistance.
  • Very high resistance to a wide range of aggressive chemicals.
  • Can be applied without risk of osmotic blistering to 'green' concrete, wet substrates or floors with no effective waterproofing membrane.
  • Excellent adhesion to dry or damp cementitious substrates.
  • Hydrates to give high early strengths, enabling rapid reinstatement of traffic.
  • Dense matrix offers low permeability to water, even at 10 bar positive and negative pressure, and very high diffusion resistance to chlorides and oxygen.

Applications:

For the protection of concrete floors and decks subject to trafficking in the most demanding internal and external environments.

Priming:

To prevent out-gassing, the substrate should be sealed with Epoprime AC.

General information
Uniclass 2015
Pr_35_31_06_80 Smoothing and levelling underlay compoundsPrimary
CAWS

M10/160 Proprietary self smoothing levelling screeds

Specification data - Smoothing and levelling underlay compounds
Product Reference

Hydroseal LX

Standard product features

Colour:

Grey.

Technical properties:

  • Application thickness: 2 mm.
  • Application temperature: 5–35°C.
  • Drying time: 2–3 hours (20°C).
  • Active ingredients: >98%.
  • Compressive strength: 55 MPa (28 days).
  • Water permeability (Taywood Test): 1.2 x 10ˆ-16 m²/sec.