Glass fibre reinforced concrete premix, for the formation of lintel heads.
For use in the formation of lintel heads.
This mix can also be used in a number of different forms including sills, copings, columns and garden features - consult manufacturer for details.
Please note, this mixture is not suitable for large sections or cladding panels.
Glass fibre reinforced concrete premix, for the formation of lintel heads.
Features and benefits:
Application:
For use in the formation of lintel heads.
This mix can also be used in a number of different forms including sills, copings, columns and garden features - consult manufacturer for details.
Please note, this mixture is not suitable for large sections or cladding panels.
| Features | Offers higher flexural strength properties than traditional semi-dry or wet cast concrete |
| Finish | Pre-finished |
| Material | Highly cement based composite manufactured from white cement, silica sand, admixtures and additives reinforced with alkali resistant glass fibre |
| Shape | Can be produced to bespoke shapes/ designs |
| Size | Can be produced to bespoke sizes |
| Uniclass 2015 |
| Product Reference | Premix GRC Lintel Heads |
| Standard | GRCA Specification for the manufacture, curing and testing of glass fibre reinforced concrete (GRC) products |
| Production method | Premix process in accordance with GRCA Specification 2017 |
| Head type | Insert requirements. |
| Guide mix design | Grade 8P |
| Dimensions | - |
| Length | Insert requirements. |
| Thickness | Insert requirements. |
| Exposed faces | - |
| Surface texture | Insert requirements. |
| Colour | BathPortlandSherwood |
| Applied surface finish | Pre-finished |
| Fixings | Insert requirements. |
| Flexural strength | After 28 days (LOP): 5 MPa. After 28 days (MOR): 8 MPa to EN 1170-5 |
| Dry density | 1850 kg/mᶟ to EN 1170-6 |
| Water absorption | 9% to EN 1170-6 |
| Standard product features | Colour: Range of three colours. Features: Offers higher flexural strength properties than traditional semi-dry or wet cast concrete. Finish: Pre-finished. Material: Highly cement based composite manufactured from white cement, silica sand, admixtures and additives reinforced with alkali resistant glass fibre. Shape: Can be produced to bespoke shapes/ designs. Size: Can be produced to bespoke sizes. |