A gutter coatings system with a ten year guarantee,
engineered using inorganic (mineral based) Alkoxy technology to prevent chalking and deterioration, with resistance to weathering from ultraviolet (UV) light, rain, snow and temperature extremes to retain high movement accommodation, flexibility and adhesion without cracking or peeling.
Installed by manufacturer network of approved contractors, all project works are inspected and certified to exacting quality standards – consult manufacturer for details.
Features and benefits:
- Delcote GS is a 100% silicone based remedial treatment and is therefore ideal for use in areas of industrial pollution and/ or coastal and marine environments.
- One component requiring no mixing and can be applied by roller or brush.
- Primer-less adhesion to most common substrates.
- Fast cure rate, 15–30-minute skin over time followed by 1–2 hour tack free time.
- Long service life with excellent resistance to UV attack.
- Does not degrade by chalking.
- Any subsequent soiling of the product can be easily removed by a simple detergent wash.
- No additional structural weight is applied.
- No disruption for building users.
System components and installation application:
- Seamsil sealant: Gun-applied around the base of the fixing and into the gutter joint, forming a complete bridged seal. To be tooled off to a neat edge. Where there are slight perforations (up to 15 mm in diameter) in the gutter joint, Seamsil sealant can be used to bridge the gap.
- Seamsil base coat: Whilst the Seamsil sealant is still wet, apply two coats of Seamsil base coat by brush at a minimum film thickness of 250 µm and allow to cure. The area to be treated should be at least 25 mm from the either side of the gutter joint and a further 10 mm beyond the prepared area, ensuring complete coverage of all exposed steel work and gutter joint bolts/ fixings.
- Delcote GS base and top coats: Utilizing roller or brush, apply a first coat of Delcote GS to prepared, clean and dry, structurally sound surfaces at a wet film thickness of 250 µm and allow to fully cure. Once the base coat is tack free (an overnight cure is recommended), apply a second coat at a wet film thickness of 250 µm and allow to fully cure.
- The product is normally applied without the need to prime.
Technical characteristics:
- Dry film thickness (complete system): gutter area: Minimum 300 µm; gutter joints: Minimum 660 µm.
Seamsil sealant:
- Chemical base: Alkoxy silicone, room temperature vulcanizing.
- Colour: Grey.
- Specific gravity 1.39.
- Shore A Hardness: 20 (approximately).
- Time to full cure: 10–14 days.
- Movement accommodation: ±50%.
- Elongation at break: 700%.
- Tensile strength: 1.6 N/mm².
- Application temperature: 3–60°C.
- Dew point: Surface to be 2°C above the dew point.
Seamsil base coat:
- Chemical base: Silicone coating in a spirit carrier.
- Specific gravity: 1.22.
- Shore A Hardness: 20 (approximately).
- Time to full cure: 10–14 days.
- Solids content: By volume – 80%.
- Movement accommodation: ±50%.
- Elongation at break: 750%.
- Tensile strength: 1.6 N/mm².
- Application temperature: 3–60°C.
- Dew point: Surface to be 2°C above the dew point.
Delcote GS base and top coats:
- Chemical base: Silicone coating in a spirit carrier.
- Specific gravity: 1.25.
- Shore A Hardness: 32 (approximately).
- Tack free: Two hours (approximately).
- Time to full cure: 7–10 days.
- Solids content: By weight – 80%, by volume – 60%.
- Elongation at break: 400%.
- Tensile strength: 1.38 N/mm².
- Application temperature: 3–60°C.
- Dew point: Surface to be 2°C above the dew point.
- Wind speed to be below 24 km/h (when spraying).