Casufloor FS is used in renovation of apartments, offices and public buildings as a levelling material. The screed is for internal use and can be covered with all common floor coverings. If a cement based adhesive or smoothing compound is required, the surface of the screed must be sealed first using an appropriate acrylic primer/ sealer. It is not suitable for wetrooms.

Description

CASEA Casufloor FS is a calcium sulfate based polymer modified, levelling screed compound, ideal for renovations or levelling cementitious, calcium sulfate and concrete based floors. The composition of the material makes it ideal to use over heated floor systems, layer thickness 2–10 mm. The material complies with BS EN 13813 and is CE marked. Designation: CA-C30-F7.

Benefits:

  • Smooth laitance free finish.
  • Next day application onto CA base screeds.
  • Pumpable - high flowability.
  • Easy trafficking.
  • Very low shrinkage.
  • Reduced drying times.
  • CE marked.
  • BS EN 13813.

Applications:

Casufloor FS is used in renovation of apartments, offices and public buildings as a levelling material. The screed is for internal use and can be covered with all common floor coverings. If a cement based adhesive or smoothing compound is required, the surface of the screed must be sealed first using an appropriate acrylic primer/ sealer. It is not suitable for wetrooms.

General information
Specification data
Product Reference

CASEA Casufloor FS

Standard product features

Technical characteristics (to EN 13813: 2002):

  • Maximum thickness: 10 mm.
  • Minimum thickness: 2 mm.
  • Use: Internal.
  • Compressive strength (28 days): ≥ 30.0 N/mm².
  • Flexural strength (28 days): ≥ 7.0 N/mm².
  • Tensile adhesion: > 1.5 N/mm².
  • Shrinkage (28 days): < 0.1%.
  • Hardening Time (light foot traffic): Approximately eight hours.
  • Hardening Time (final strength): After 24 hours depending on thickness and site conditions.
  • Recommend water content: 26%.
  • Water requirement: Approximately 6.5 L per 25 kg bag.
  • Reaction to fire: A1 non-combustible.
  • Thermal conductivity: λR=1.40 W/mK.
  • Yield: 1.5 kg/mm/m².
  • Modulus of elasticity: 18 kN/mm².
  • Flow rate: 240–260 mm.

Digital objects
PlatformCompatibleVersionCertified to
IFC
IFC2X3 5 1.3
ARCHICAD
- 1.0
Vectorworks
- 1.0
AECOsim
- 1.0
Revit
Revit 2016 6 2.0
Download now from NBS National BIM Library
Similar products from SMET Building Products Ltd