Suitable for use in watertight construction joints and for the bonding and sealing of various substrates used within the building industry. Provides primerless adhesion to:

  • Glass.
  • Anodized aluminium.
  • Wood.
  • Lacquered metal.
  • Concrete.
  • Stone.

Should not be applied in temperatures below 5°C.

Description

One-component, ready-to-use, multi-purpose adhesive and sealant.

Features and benefits:

  • Elastomeric properties.
  • Non-sag.
  • Low skin formation and fast moisture curing.
  • High elasticity.
  • Good recovery.
  • Tear-resistant.
  • Can withstand various weather conditions.
  • Applicable by pneumatic equipment or a handgun.

Applications:

Suitable for use in watertight construction joints and for the bonding and sealing of various substrates used within the building industry. Provides primerless adhesion to:

  • Glass.
  • Anodized aluminium.
  • Wood.
  • Lacquered metal.
  • Concrete.
  • Stone.

Should not be applied in temperatures below 5°C.

General information
Specification data
Product Reference

Surestop Adhesive

Accessories/ Other requirements

Not required

Surestop Barrel Gun and Nozzles

Surestop BWB

Sealing construction joints.

Surestop Voidformer

Standard product features

Colour:

Grey.

Technical characteristics:

  • Coverage: 5 lm (per 600 ml, at the required thickness of 10 mm).
  • Form: Paste.
  • Application temperature: 5–35°C.
  • Density (at 20°C): 1.34–1.36.
  • Sagging (to ISO 7390): <2 mm.
  • Skin formation time (at 23°C, 50% RH): 20–30 minutes.
  • Cure formation time (at 23°C, 50% RH): >3 mm (after 24 hours).
  • Shore A hardness (after ISO 868, 3 seconds): >50 (after 14 days).
  • Volume loss (to ISO 10563): <2%.
  • Temperature resistance: -40°C to 100°C (for cured sealant).
  • UV resistance: Excellent.
  • Shrinkage: 7% (approximately).
  • Weathering resistance: Excellent.
  • Staining: None.
  • Chemical resistance: Good resistance to water, diluted acids and diluted alkalines.
  • Modulus of elasticity (to ISO 37): At 100%: 1 MPa (approximately); at break: 1.8 MPa.
  • Elongation at break (to ISO 37): >300%.
  • Tear strength (to ISO 34): 10 N/mm (approximately).